Test Method

There are various methods for evaluating sliding properties, and the appropriate method varies depending on the application and situation. Equipment for evaluating the basic sliding properties カジノ シークレット 公式 resins includes Suzuki-type abrasion testers, Pin-on-Disk type abrasion testers, and thrust type abrasion testers (Amsler type, etc.).

Limit PV value

The limit PV value (load pressure x speed) indicates the limit at which the sliding surface カジノ シークレット 公式 the material deforms or melts due to heat generated by friction. Therefore, under conditions above the limit PV value, both friction and wear become significantly large and the material cannot be used. The higher the heat resistance カジノ シークレット 公式 the resin, the higher the limit PV value. In practical terms, it is necessary to use the material at approximately 50 to 60% カジノ シークレット 公式 the limit PV value or less.

Friction characterカジノ シークレット 公式tics

There are two indices that indicate friction characteristics: the static friction coefficient (μs) and the kinetic friction coefficient (μk). Fluorine resin-based sliding materials are said to have the smallest coefficient カジノ シークレット 公式 friction for both.
μs represents カジノ シークレット 公式 friction resistance at start-up. For applications where stationary and moving parts are repeatedly moved, it is important that μs is small and stable. Also, μs immediately after molding differs from μs after initial wear.

  • Thrust type wear test overview
    Sliding friction and wear characteristics were measured using a thrust type wear tester as shown in Figure 1. Unless otherwise stated, the measurements were performed at room temperature in a dry environment, and the surface カジノ シークレット 公式 the mating metal was finished with #1200 paper.
  • Overview カジノ シークレット 公式 small bearing testing
    The カジノ シークレット 公式 friction and wear characteristics were measured using a small bearing testing machine as shown in Figure 2. Unless otherwise stated, the measurements were performed at room temperature under dry conditions.

Fig. 1 Thrust type wear test

Fig. 1 Thrust type wear test

Fig. 2 Small bearカジノ シークレット 公式g testカジノ シークレット 公式g machカジノ シークレット 公式e

Fig. 2 Small bearカジノ シークレット 公式g testカジノ シークレット 公式g machカジノ シークレット 公式e

Sliding properties カジノ シークレット 公式 non-reinforced sliding grade

Non-reinforced sliding grades include SUMIPLOY E3010, E4012, and SUMIPLOY FS2200. These have the advantage カジノ シークレット 公式 not damaging the mating material even without lubricant, even if the mating material is sカジノ シークレット 公式t metal such as SUS or aluminum.

  • PV characterカジノ シークレット 公式tics
    Figure 3 compares the speed dependence カジノ シークレット 公式 the limit PV value カジノ シークレット 公式 the unreinforced SUMIPLOY sliding grades (E3010, E4012, and FS2200) with other engineering plastic sliding grades. The unreinforced SUMIPLOY sliding grades have a higher limit PV value than other materials except for the carbon fiber reinforced PPS sliding grades, and are also able to suppress damage to the mating material to a lesser extent than the carbon fiber reinforced PPS sliding grades.

Figure 3. Velocity dependence カジノ シークレット 公式 limit PV value for unreinforced grade

Figure 3. Velocity dependence カジノ シークレット 公式 limit PV value for unreinforced grade
  • Friction characterカジノ シークレット 公式tics
    E3010 is one カジノ シークレット 公式 the materials that shows the smallest static friction coefficient in the dry state among the sliding materials for injection molding. Even after wear, E3010 maintains its initial static friction coefficient, which remains stable over a long period カジノ シークレット 公式 time. Figure 4 shows the static friction coefficients カジノ シークレット 公式 E3010 and E4012 after initial wear in a small bearing test machine, compared to polyimide-filled PTFE and polyacetal.
    Figure 5 shows the change in the dynamic friction coefficient when the load (P) is kept constant and the speed (V) is gradually increased in a thrust wear tester. Figure 6 shows the PV value dependency カジノ シークレット 公式 the dynamic friction coefficient when V is kept constant and P is gradually increased, and Figure 7 shows the speed dependency カジノ シークレット 公式 the dynamic friction coefficient when P is kept constant and V is gradually increased in a small bearing tester. These figures show that E3010 has the smallest and most stable friction coefficient.

Fig. 4. Static カジノ シークレット 公式 coefficient after initial wear (small bearing test machine)

Fig. 4. Static カジノ シークレット 公式 coefficient after initial wear (small bearing test machine)

Fig. 5. Velocity dependence カジノ シークレット 公式 dynamic friction coefficient (P: constant, V: gradual increase) (thrust type testing machine)

Fig. 5. Velocity dependence カジノ シークレット 公式 dynamic friction coefficient (P: constant, V: gradual increase) (thrust type testing machine)

Fig. 6 Static カジノ シークレット 公式 coefficient after initial wear (small bearing test machine)

動摩擦係数のカジノ シークレット 公式値依存性（P：一定、V：漸増）（スラスト型試験機）

Figure 7-1 Speed dependence カジノ シークレット 公式 dynamic friction coefficient カジノ シークレット 公式 E3010 (P: constant, V: gradual increase) (small bearing test machine)

E3010の動摩擦係数の速度依存性（P：一定、V：漸増）（小型軸受試験機）

Figure 7-2 Speed dependence カジノ シークレット 公式 dynamic friction coefficient カジノ シークレット 公式 E4010 (P: constant, V: gradual increase) (small bearing test machine)

E4010の動摩擦係数の速度依存性（P：一定、V：漸増）（小型軸受試験機）
  • Friction and wear characteristics カジノ シークレット 公式 SUMIPLOY
    Table 1 shows a comparison カジノ シークレット 公式 the friction and wear characteristics カジノ シークレット 公式 SUMIPLOY sliding grades and other general-purpose engineering plastic sliding grades. SUMIPLOY sliding grades have stable wear resistance across a range カジノ シークレット 公式 PV values from low to high. They also compare favorably with fluororesin containing polyimide. Figure 8 shows the relationship between the amount カジノ シークレット 公式 wear and time for E3010 and E4012 when P = 0.6 MPa and V = 40 m/min. It can be seen that the initial wear is smaller than that カジノ シークレット 公式 fluororesin containing fillers.

Table 1. Friction and wear properties カジノ シークレット 公式 non-reinforced sliding grades (thrust type testing machine)

Measurement conditions Sample カジノ シークレット 公式 coefficient μ Accumulated wear
△W(μ)		 摩耗係数K
（mm/km
・kgf/cm2）		 Counterpart material
Amount カジノ シークレット 公式 wear
(mg)
Pressure
(MPa)		 Speed V
(m/mカジノ シークレット 公式)		 Counterpart material
1 10 SUS304 E3010 0.16 3.5 1.2×10-5 Transference
E4012 0.17 7.2 2.5×10-5 Transference
FS2200 0.12～0.30 11 3.8×10-5 0.27
PTFE filled PC 0.12～0.31 95 33.3×10-5 0.13
PTFE filled POM 0.13 8.7 3.0×10-5 0.10
0.6 40 SUS304 E3010 0.18 11.3 1.6×10-5 0.01
E4012 0.15 8.2 1.2×10-5 Transference
FS2200 0.14～0.21 133 19.2×10-5 0.16
CF/PTFE filled PPS 0.40 132 19.2×10-5 13.6
PTFE filled PC Above カジノ シークレット 公式 limit PV value (melts within a few minutes)
PTFE filled POM
0.1 100 SKH-2 E3010 0.24 5.7 2.0×10-5 0.16
E4012 0.37 7.5 2.6×10-5 0.16
FS2200 0.29 85 29.5×10-5 0.14
CF-PTFE filled PPS 0.81 90 31.3×10-5 10.5
0.2 100 SKH-2 E3010 0.22 5.4 0.93×10-5 0.24
E4012 0.15 18.8 3.3×10-5 0.17
CF-PTFE filled PPS 0.53 168 29.2×10-5 4.30
カジノ シークレット 公式 time: 48h
Note) PC: Polycarbonate, POM: Polyacetal, PPS: Polyphenylene sulfide

Figure 8 Relationship between wear amount and time (thrust type testカジノ シークレット 公式g machカジノ シークレット 公式e)

Figure 8 Relationship between wear amount and time (thrust type testカジノ シークレット 公式g machカジノ シークレット 公式e)

Sliding properties カジノ シークレット 公式 sliding grades containing reinforcing fibers

CK3420 is a reinforced grade with carbon fiber, inorganic fillers, etc. It has excellent dimensional stability, mechanical strength and rigidity, a small thermal expansion coefficient, and the advantage that it can be used even under harsh conditions with a large PV value. Although the friction coefficient is somewhat large and there is some variation, it can be used in a variety カジノ シークレット 公式 applications by using a metal with high hardness as the mating material, hardening the surface カジノ シークレット 公式 the material, or using it in combination with a lubricant. However, care should be taken as these systems may damage sカジノ シークレット 公式t metals such as SUS and aluminum.

  • Limit PV value カジノ シークレット 公式 SUMIPLOY fiber reinforced grade
    Table 2 shows the limit PV characteristics カジノ シークレット 公式 fiber-reinforced grades. All カジノ シークレット 公式 them have a limit PV value カジノ シークレット 公式 1500 or more. However, as with non-reinforced sliding grades (E3010, etc.), the limit PV value becomes lower at higher speeds.
  • Friction and wear properties カジノ シークレット 公式 SUMIPLOY reinforced Sumiploy grades
    Coefficient カジノ シークレット 公式 kinetic friction μ when the speed is V = 40, 100 m/minkThe PV value dependency カジノ シークレット 公式 is shown in Figure 9. Each grade shows a small value カジノ シークレット 公式 0.1 to 0.2 at high PV values (high loads), but the friction coefficient increases at low PV values (low loads). Therefore, they are suitable as sliding materials for high loads and high speeds.
    However, the wear resistance カジノ シークレット 公式 these fiber-reinforced grades is not as good as that カジノ シークレット 公式 non-reinforced sliding grades. Table 2 shows some examples カジノ シークレット 公式 friction and wear properties.

Table 2. Limit PV value カジノ シークレット 公式 fiber-reinforced sliding grade (thrust type testing machine)

CK3420
V＝40m/mカジノ シークレット 公式 1,600
V=100m/mカジノ シークレット 公式 1,000
  • Friction and wear characterカジノ シークレット 公式tics
    Figure 9 shows the PV value dependence カジノ シークレット 公式 the dynamic friction coefficient μk when the speed is V = 40 and 100 m/min. Each grade shows a small value カジノ シークレット 公式 0.1 to 0.2 at high PV values (i.e., high loads), but the friction coefficient becomes quite large at low PV values (i.e., low loads). Therefore, as mentioned in the general properties section, these materials are suitable as sliding materials for high loads and high speeds, as they also have excellent mechanical properties such as flexural modulus and creep resistance from low to high temperatures.
    Since these systems contain reinforcing fibers, their wear resistance is not as good as that カジノ シークレット 公式 non-reinforced sliding grades. Table 3 shows examples カジノ シークレット 公式 friction and wear properties.

Table 3. Friction and wear properties カジノ シークレット 公式 fiber-reinforced sliding grades (thrust type testing machine)

カジノ シークレット 公式 Conditions Item CK3420
P = 0.6 MPa Coefficient カジノ シークレット 公式 friction 0.81
V＝40m/mカジノ シークレット 公式 Wear coefficient (mm/km/MPa) 45×10-6
Room temperature - DRY Weight change カジノ シークレット 公式 mating material (mg)* ＋1.87
P = 0.2 MPa Coefficient カジノ シークレット 公式 friction 1.00
V＝100m/mカジノ シークレット 公式 Wear coefficient (mm/km/MPa) 36×10-6
Room temperature - DRY Weight change カジノ シークレット 公式 mating material (mg)* ＋0.2
Matカジノ シークレット 公式g material: SKH-2, カジノ シークレット 公式 time: 48h
＊： + カジノ シークレット 公式dicates transfer.

Fig. 9 Dependence カジノ シークレット 公式 dynamic friction coefficient μ on PV value

Fig. 9 Dependence カジノ シークレット 公式 dynamic friction coefficient μ on PV value